Abstract
AbstractPolypropylene (PP) is a classical organic material for dielectric capacitor, exhibiting typical linear charge–discharge characteristics. However, its low energy density fails to meet the operating requirements of high‐power and energy storage systems. In this study, techniques such as spray‐coating, lamination hot‐pressing, melt blending, and in situ melt‐drawing are employed to fabricate PP‐based sandwich‐structured composite dielectrics. The outer layers consist of BN nanosheets (BNNSs)/PP composite, while the middle layer comprises Ba0.7Sr0.3TiO3@Polydopamine (BST@PDA)/PP. The introduction of BNNSs with a wide bandgap improves the breakdown strength of composites. BST@PDA increases the overall polarization of the composites and alleviates the local electric field concentration caused by hetero‐interfacial field distortion. When the filling concentration of BNNSs is 0.10 wt% and that of BST@PDA nanowires is 3 wt%, the composite demonstrates a high dielectric constant and low dielectric loss. Additionally, the sandwich‐structured composite, exhibiting a high charge–discharge efficiency of 97.80%, presents enhanced breakdown strength (Eb ~ 453 MV/m) and increased energy storage density (Ue ~ 5.67 J/cm3), which are 39.38% and 189.29% higher than neat PP (325 MV/m, 1.96 J/cm3), respectively. This study offers a viable and efficient approach to augment the energy storage density of PP‐based dielectrics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.