Abstract
In this study, we developed a composite material comprising UIO-66-NH2 encapsulated tannic acid (TA) loaded on Ti3C2Tx to improve the corrosion resistance of water borne epoxy (WEP) coatings. The successful synthesis of the material was determined by FT-IR, XRD, XPS, EDS, TGA, SEM and TEM characterization. Furthermore, ultraviolet (UV)tests were conducted to evaluate the release rate of TA at varying pH levels, revealing a release rate of approximately 95 % at pH 2. Electrochemical impedance spectroscopy (EIS) results over 60 d indicated that the Rc value of TU-T/WEP remained unchanged at 3.934 × 108, demonstrating a two-order magnitude increase compared to those of pure epoxy coatings, attributed to the synergistic active and passive protection of TU-T materials. The self-healing ability of the TU-T/WEP coating was validated through manual scratch experiments. Additionally, the EIS test showed that the Rc value of TU-T/WEP coating increased to 3.5 × 105 after 72 h, representing a two-order magnitude increase over that of the WEP coating alone. This study introduces a novel approach using green tannic acid as a corrosion inhibitor and amino-functionalized Ti3C2Tx with UIO-66-NH2 to enhance corrosion resistance and self-healing aproperties of coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.