Abstract
A NASICON-type sodium-ion conducting material was synthesized via the glass-ceramic route by investigating the zinc doped Na2O–Al2O3–TiO2–P2O5 system. The glasses and glass-ceramics corresponding to the formula Na2+xAl1-xZnxTi(PO4)3 (x = 0, 0.2, 0.4, 0.6, 0.8, 1), labeled as (NAZTP-Gx) and (NAZTP-GCx) respectively, were characterized using different techniques. Differential Scanning Calorimetry (DSC) measurements were carried out to identify the characteristic temperatures, the glass transition (Tg) and the crystallization temperature (Tc). X-ray Diffraction (XRD) analysis of the glass-ceramics confirmed the formation of a solid solution Na2+xAl1-xZnxTi(PO4)3 NASICON phase, Theoretical calculations employing the Perdew–Burke–Ernzerhoff generalized gradients approximation (PBE-GGA) model supported the potential substitution of aluminum by zinc in the octahedral site in the NASICON-phase. Further structural insights were obtained through Infrared (IR) and Raman spectroscopies. Scanning electron microscopy (SEM) analysis revealed a distinct flower-like shape of the formed crystallites in the glass-ceramic NAZTP-GC0.2. Electrical characterization using electrochemical impedance spectroscopy (EIS) demonstrated that the NAZTP-GC0.2 sample exhibited the highest ionic conductivity at 300 °C, reaching 4.1 × 10−5 (Ω−1 cm−1) with an activation energy of 0.25 eV. The DC polarization was performed on the NAZTP-GC0.2 glass-ceramic, revealing that the ions are the main charge carriers in the sample. This comprehensive analysis provides valuable insights into the partial zinc doping of NASICON glass-ceramics, offering potential for improved performance as solid electrolytes in various applications.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.