Enhancement of self-healing to mechanical properties of concrete

Abstract

Concrete is the main construction material of many structures. Exposing to loads creates cracks in concrete, which reduce the performance and durability. The decrease of concrete cracks becomes a necessity demand to ensure more durability and structural integrity of the concrete structure. Autogenous healing concrete is a kind of new smart concretes, which has the ability to reclose its cracks by means of itself. Concrete self-healing is a type of free repairs processes, which is reduce direct and indirect cost of maintenance and repairing. This work targets to inspect the mechanical properties of concrete after using two combinations of two materials (20 kg/m3 calcium hydroxide Ca(OH)2 and 2 kg/m3 sodium carbonate Na2CO3 and 30 kg/m3 calcium hydroxide and 3 kg/m3 sodium carbonate) as a partial replacement of cement to work as self-healing agents. The paper reports and study the compressive, flexural and splitting tensile strengths and ultrasonic pulse velocity tests’ results at 7, 28 and 90 days of concrete age. Use of two combinations of calcium hydroxide and sodium carbonate, as healing agents, enhanced the mechanical properties of concrete and reduced the width of concrete cracks with time. The concrete compressive strength was increased after curing for 90 days by 9.3 and 11.1 %, respectively. The flexural strength was improved by 14.3 and 15.9 %, respectively. Also, the splitting tensile strength was enhanced by 6.9 and 9.3 %, respectively.