AbstractThe effect of plastic deformation of austenite on the nucleation of pearlite was investigated using an Fe–12Mn–0.8C (mass%) alloy. Slight warm deformation of austenite prior to pearlite transformation effectively accelerates the intragranular nucleation of pearlite although intragranular pearlite is hardly formed without deformation. Formation of pearlite at annealing twin boundaries is promoted in the warm‐rolled specimens. Additionally MnS particles are activated as intragranular nucleation sites of pearlite. Cold rolling of austenite introduces many deformation twins in the alloy used. Subsequent isothermal transformation heat treatments result in nucleation of pearlite at intersections of the deformation twins. It is concluded that incoherent portions introduced by deformation onto the annealing or deformation twin boundaries are effective nucleation sites in the pearlite transformation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.