Abstract
Al0.4FeCrCo1.5NiTi0.3 high-entropy alloy (HEA) was prepared by mechanical alloying (MA) and spark plasma sintering (SPS), which were evaluated in this study by XRD and TEM. After SPS, the bulk alloy exhibited a structure with a dominant fcc phase, a minor volume fraction of bcc phase, and the formation of TiAl3 intermetallic compound. Deformation twinning was observed in the fcc phase in the bulk HEA. The latter had a compressive strength, strain and Vickers hardness of 2225 ± 15 MPa, 17.52 ± 0.50 % and 515 ± 16 HV, respectively. The corrosion resistance studies indicated that Al0.4FeCrCo1.5NiTi0.3 with ultra-fine grained micro-structure was easier to passivate and possessed excellent corrosion resistance. DOI: http://dx.doi.org/10.5755/j01.ms.25.3.19452
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.