Abstract
Magneto-optical materials based on Tb3Ga5O12 (TGG) crystals are providing promising opportunities for modern Faraday isolators (FIs). Tb2.85Er0.15Ga5O12 crystals with high transmittance were prepared using the Czochralski method (Cz). It is noted that as-prepared crystal presents an extremely low absorption coefficient of 1270 ppm/cm at 1064.0 nm and the Verdet constants of as-grown crystal at 405.0, 533.0, 632.0, 1064.0 nm were 588.0, 230.2, 152.3, and 51.7 rad m−1 T−1, respectively. The measured Verdet constant at 1064 nm was about 1.3 times higher than that of pure TGG crystal. Thus, it has the possibility to minimize the length and the magnet of faraday rotator in making FIs. The Excellent characteristic makes Tb2.85Er0.15Ga5O12 single crystal an attractive magneto-optical material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.