Abstract
Nanosize grains of ~ 65 nm were developed with large misorientation angles of grain boundaries in surface region of normalized and tempered modified 9Cr-1Mo steel by ultrasonic shot peening (USSP) with hard steel balls of 3 mm diameter. The surface roughness and the depth of nanostructured surface region were found to increase with the duration of USSP from 0.5 to 5 min. Hot corrosion tests were performed for the Un-USSP and the samples USSPed for the durations of 0.25 and 1.5 min and also for the samples subjected to USSP and subsequently pre-oxidation at 600 °C for 4 h. The hot corrosion resistance at 600 °C under 100% NaCl coating was significantly improved by USSP for 1.5 min and subsequent pre-oxidation at 600 °C for 4 h. The results are discussed in terms of the formation of more uniform and effective protective iron–chromium oxide layer on the USSPed surface from the subsequent pre-oxidation treatment, prior to hot corrosion of the specimens under 100% NaCl coating at 600 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.