Enhancement of hole-injection and power efficiency of organic light emitting devices using an ultra-thin ZnO buffer layer

Abstract

The advantages of using an anode buffer layer of ZnO on the electro–optical properties of organic light emitting devices (OLEDs) are reported. ZnO powders were thermal-evaporated and then treated with ultra-violet (UV) ozone exposure to make the ZnO layers. The turn-on voltage of OLEDs decreased from 4 V (4.2 cd/m 2) to 3 V (3.4 cd/m 2) and the power efficiency increased from 2.7 lm/W to 4.7 lm/W when a 1-nm-thick ZnO layer was inserted between indium tin oxide (ITO) anodes and α-naphthylphenylbiphenyl diamine (NPB) hole-transporting layers. X-ray and ultra-violet photoelectron spectroscopy (XPS and UPS) results revealed the formation of the ZnO layer and showed that the work function increased by 0.59 eV when the ZnO/ITO layer was treated by UV-ozone for 20 min. The surface of the ZnO/ITO film became smoother than that of bare ITO film after the UV-ozone treatment. Thus, the hole-injection energy barrier was lowered by inserting an ZnO buffer layer, resulting in a decrease of the turn-on voltage and an increase of the power efficiency of OLEDs.