Abstract
Abstract Zn 0.98 Cu 0.02 O and Zn 0.95 Cu 0.02 Co 0.03 O powders were synthesized by sol–gel method, and the effects of Co codoping on the structure, optical and magnetic properties of the Zn 0.98 Cu 0.02 O powders were studied in detail. The X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) measurement shows the Zn 0.98 Cu 0.02 O and Zn 0.95 Cu 0.02 Co 0.03 O powders were single phase with the ZnO wurtzite structure, and there was no ferromagnetic-related secondary phase in these powders. Moreover, these powders exhibited ferromagnetism at the room temperature investigated by the magnetic measurement, and the ferromagnetism of the Zn 0.98 Cu 0.02 O and Zn 0.95 Cu 0.02 Co 0.03 O samples were originated from the fact that the Cu ions and Co, Cu ions doped into the ZnO lattices, respectively. In addition, the saturation magnetization (Ms) was significantly increased with Co codoping due to the increased density of oxygen vacancies.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.