Abstract
An excellent combination of elongation over 30% and high strength about 100kgf/mm2 is achieved in processing of a 0.4C-1.5Si-0.8Mn steel by intercritical annealing, rapid cooling into bainite transformation temperature to soak several minutes. This combination is caused by transformation induced plasticity of retained austenite. Sufficient amount of stable austenite is a requisite for the good ductility. For the rapid cooling after annealing, the soaking temperature for the best combination of strength and ductility is immediately above Ac1. On the other hand, a delay before rapid cooling provides good properties if the soaking temperature is near Ac3 and the subsequent cooling is performed at a lower rate before pearlite transformation; in this case the critical cooling rate is reduced. These phenomena are discussed in terms of the growth of ferrite and the diffusion of alloying elements inclusive of Mn during slow cooling.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of the Iron and Steel Institute of Japan
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.