Abstract
Polyaniline-based cryogels were prepared by oxidative cryopolymerization in the presence of various concentrations of poly(N-vinylpyrrolidone) and phytic acid used as a polymer support and a dopant, respectively. Mechanical strength and handling stability of the resulting macroporous materials (pore size up to 70 μm) were significantly improved by the addition of poly(N-vinylpyrrolidone) into the polymerization system compared to the cryogels crosslinked only by phytic acid. Increase of poly(N-vinylpyrrolidone) concentration in the reaction medium above 5 wt%, while not noticeably changing mechanical properties, was found to lead to a decrease of conductivity and specific surface area. Introduction of optimal amount of phytic acid (0.2 M) as an additional codopant, in opposite, allowed enhancement of the material conductivity and specific surface area as well as increase of their tensile modulus. Polyaniline-poly(N-vinylpyrrolidone) cryogels containing phytic acid also showed better cytocompatibility due to lower cytotoxicity and improved cell adhesion and proliferation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.