Abstract
Sn-doped gallium oxide (Ga2O3) wrap-gate fin-array field-effect transistors (finFETs) were formed by top-down BCl3 plasma etching on a native semi-insulating Mg-doped (100) β-Ga2O3 substrate. The fin channels have a triangular cross-section and are approximately 300 nm wide and 200 nm tall. FinFETs, with 20 nm Al2O3 gate dielectric and ∼2 μm wrap-gate, demonstrate normally-off operation with a threshold voltage between 0 and +1 V during high-voltage operation. The ION/IOFF ratio is greater than 105 and is mainly limited by high on-resistance that can be significantly improved. At VG = 0, a finFET with 21 μm gate-drain spacing achieved a three-terminal breakdown voltage exceeding 600 V without a field-plate.
Highlights
by top-down BCl3 plasma etching on a native semi-insulating Mg-doped
a wide range of n-type doping achievable by halide vapor phase epitaxy
The first transistor devices by homoepitaxial Ga2O3 were demonstrated with a Sn-doped Ga2O3 channel grown by
Summary
Sn-doped gallium oxide (Ga2O3) wrap-gate fin-array field-effect transistors (finFETs) were formed by top-down BCl3 plasma etching on a native semi-insulating Mg-doped (100) b-Ga2O3 substrate.
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.