Abstract
The investigation is focussed on phase generation and magnetocaloric properties of a series of Ni77-XMnXGa23 (x=22, 23, 24, 25, 27) alloys prepared through arc melting furnace. With increase in Mn content, the alloys showed systematic transition from a non-modulated martensite (NM) to a fully austenitic parent phase through an appearance and coexistence of modulated (M) structure. Intermediate Mn containing alloy (#Mn24) not only displayed high magnetic entropy change (ΔSM) of −7.7J/kg−1K−1 but also large Refrigerant Capacity (RC) of 169J.Kg−1 at magnetic field change of 3 T compared to other alloys. The coexisting martensite (NM, M) and parent austenite as well as overlapping thermomagnetic and structural transformation was deliverable through tuning of alloy chemistry wherein Ni was systematically substituted by Mn. Transmission electron microscopy (TEM) supported the proposition with existence of martensite plates of different morphology in Mn24 alloy exhibiting superior magnetocaloric properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.