Graphene oxide (GO) has been proved to be a potential reinforcement. In this paper, 0.3 wt%, 0.6 wt%, and 1.0 wt% GO reinforced Fe22Co24Cr20Ni23Al11 high-entropy alloy (HEA) composites and pure HEA were synthesized by spark plasma sintering (SPS) to improve the surface properties of HEA. The surface properties including hardness and wear resistance of various samples were comparatively investigated. The experimental results indicated that the surface hardness and wear resistance were enhanced as the content of GO increased (when the GO content was less than 0.6 wt%), which were attributed to the grain refinement strengthening and lubrication effect of GO. However, as the content of GO incrementally increased to 1.0 wt%, the hardness exhibited a descending trend and the coefficient of friction (COF) increased, resulting from the agglomeration of GO. Accordingly, the residual indentation and wear track of HEA/0.6 wt% GO exhibited a minimum depth, which further confirmed the results of the nanoindentation and wear tests.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.