Abstract
The sintering of TiB2 was limited due to its high degree of covalent bonding and low self diffusion coefficient. To solve this problem, hot pressing has been used for fabricating TiB2 ceramics, but this process was expensive and limited to the production of simple shapes. Pressureless sintering has also been studied, but its sintering temperatures is, as high as more than 2000°C, resulting in exaggerated grain growth and decrease of mechanical properties. The addition of SiC was found to be effective in improving the densification. However, a supplementary HIP process was needed to enhance the mechanical properties. In this study, the densification behavior and microstructural change of TiB2 ceramics infiltrated by the polycarbosilane of SiC precusor were investigated. The infiltrated polycarbosilane was converted to SiC during heating and densification was accelerated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.