Enhanced red emission of 808 nm excited upconversion nanoparticles by optimizing the composition of shell for efficient generation of singlet oxygen

Abstract

With the aim to enhance the upconversion luminescence (UCL) intensity, much attention was paid to reduce the energy-back transfer from Er3+ ions to Nd3+ ions by constructing various kinds of multilayer upconversion nanoparticles (UCNPs). However, the energy-back transfer was difficult to be completely eliminated. Also, the thick shell of multilayer UCNPs is not favourable for effective Förster resonance energy transfer (FRET) in photodynamic therapy (PDT) system. Herein, an effective and facile method was applied to prepare UCNPs by optimizing the composition to largely enhance the red emission (at 660 nm) for efficient generation of singlet oxygen (1O2). In detail, the concentrations of Nd3+ ions and Yb3+ ions doped in the sensitizing shell were systematically researched to balance the energy back-transfer and the light harvest ability. The optimal emission and a relatively high Red/Green (R/G) ratio of NaYF4:Yb,Er,Nd@NaYF4:Yb0.1Nd0.2 UCNPs were obtained simultaneously. Furthermore, the emission under 980 nm excitation demonstrated the energy back-transfer from Er3+ to Yb3+ ions was also notable which was largely ignored previously. Then, UCNPs were encapsulated into mesoporous silica shell, and the photosensitizer Chlorin e6 (Ce6) was covalently conjugated to form a non-leaking nanoplatform. The efficiency of 1O2 generation obviously increased with the enhanced emission of UCNPs.