Abstract
Indium tin oxide/silver/indium tin oxide (ITO/Ag/ITO) multilayers have attracted much attention to fulfill the growing need for high-performance transparent conducting oxide electrodes. To make these transparent multilayers work better, electro-annealing, which is a method of self-heating by electric current, can be effective. Moreover, the effect of current on ITO/Ag/ITO multilayers should be investigated to make sure that electronic devices will be reliable over their lifetime. In this study, ITO/Ag/ITO multilayer electrodes with varying Ag thicknesses were grown by DC magnetron sputtering at room temperature. Structural, optical, and electrical properties of these multilayers were investigated before and after electro-annealing. Measurement results revealed that improved optical transmittance and sheet resistance can be obtained by the optimization of Ag thickness for the as-grown ITO/Ag/ITO layers. The highest figure of merit (FoM) value of 17.37 × 10−3 Ω−1 with optical transmittance of 85.15% in the visible region and sheet resistance of 11.54 Ω/□ was obtained for the Ag thickness of 16.5 nm for as-grown samples. The electro-annealing of as-grown ITO/Ag/ITO multilayers led to improved optical behavior of the multilayer structure over a wide spectral range, especially in the near-infrared range. Electro-annealing also provided an improvement in the crystallinity and sheet resistance of the electrodes. The improvement of the electrical and optical properties of the structure enabled a FoM of 23.07 × 10−3 Ω−1 with the optical transmittance of 86.80% in the visible region and sheet resistance of 10.52 Ω/□. The findings of this work provide proper knowledge of the properties of ITO/Ag/ITO multilayers under electrical current and suggest that the overall performance of the multilayers can be improved by the electro-annealing process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.