Abstract

Low-temperature solution-processed oxide semiconductor and dielectric films typically possess a substantial number of defects and impurities due to incomplete metal-oxygen bond formation, causing poor electrical performance and stability. Here, we exploit a facile route to improve the film quality and the interfacial property of low-temperature solution-processed oxide thin films via elemental diffusion between metallic ion-doped InOx (M:InOx) ternary oxide semiconductor and AlOx gate dielectric layers. Particularly, it was revealed that metallic dopants such as magnesium (Mg) and hafnium (Hf) having a small ionic radius, a high Gibbs energy of oxidation, and bonding dissociation energy could successfully diffuse into the low-quality AlOx gate dielectric layer and effectively reduce the structural defects and residual impurities present in the bulk and at the semiconductor/dielectric interface. Through an extensive investigation on the compositional, structural, and electrical properties of M:InOx/AlOx thin-film transistors (TFTs), we provide direct evidences of elemental diffusion occurred between M:InOx and AlOx layers as well as its contribution to the electrical performance and operational stability. Using the elemental diffusion process, we demonstrate solution-processed Hf:InOx TFTs using a low-temperature (180 °C) AlOx gate dielectric having a field-effect mobility of 2.83 cm2 V-1·s-1 and improved bias stability. Based on these results, it is concluded that the elemental diffusion between oxide semiconductor and gate dielectric layers can play a crucial role in realizing oxide TFTs with enhanced structural and interfacial integrity.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.