Abstract
Solid-state hydrogen storage alloys are becoming a practical method to transport and utilize hydrogen as fuel for various technologies. In this paper, the kinetics and capacity of hydrogen desorption from Mg-based alloys have markedly been enhanced by tuning the surface composition of alloy particles. Mg2Ni–Ct, x composites (where t refers to the pregrinding time and x to the Brunauer–Emmet–Teller specific surface area) were prepared by ball-milling the alloy in the presence of preground graphite, and Pd-coated Mg2Ni alloy powders were obtained by controlled chemical deposition of Pd on the alloy surface. We have found that the optimization of the pregrinding step of carbon is a determinant factor in enhancing the hydrogen desorption capacity of the Mg2Ni–10 wt.% C10,320 composites to 2.6 wt.% at 150 °C, the maximum performance so far reported on desorption for Mg-based alloys. Such value can even be raised to 2.8 wt.% by applying Pd deposition on the composite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.