Abstract
Mixtures of light metal borohydrides M(BH4)n, M = Li, Na, Mg, Ca and reduced graphene oxide (rGO) or graphite with molar ratio 70:30 were prepared by high energy ball milling. Samples were investigated with thermal programmed desorption (TPD) volumetric analysis to test their gas release profiles.The presence of rGO led to a lower decomposition temperature for every mixture and to a different gas-release profile compared to pristine borohydrides and mixtures with graphite. The onset of decomposition temperature was reduced by 200 °C for LiBH4, 360 °C for NaBH4, 130 °C for Mg(BH4)2 and 50 °C for Ca(BH4)2.The comparison of XRD profiles of decomposed samples showed a different pattern for each metal cation, confirming an interaction of the decomposition products with rGO sheets and suggesting a different pathway for the decomposition reaction.Reduced graphene oxide was prepared by clean thermal treatment in H2 atmosphere from graphene oxide obtained by modified wet chemical synthesis, and its presence significantly affected the gas release performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.