Abstract
In the present study, the influence of aluminium (Al) addition on the martensite-austenite phase transformation and exchange bias of Ni–Mn–Sb films have been investigated. Ni–Mn–Sb–Al films with different Al concentration (∼0–5.6%) were deposited by co-sputtering of Ni–Mn–Sb and Al targets. Experimental results revealed the decrease in martensitic transformation temperature with increasing Al content upto a certain extent (3.3%) beyond which martensitic transformation was suppressed. Paramagnetic to ferromagnetic transition temperature (TC) also decreased with increasing Al concentration. Ni50Mn36.3Sb10.4Al3.3 thin film showed significant improvement in exchange bias field as compared to pure Ni50.3Mn36.9Sb12.8 thin film. This enhancement in the exchange bias field HEB = 611 Oe at 10 K is attributed to the increase of AFM-FM interactions that result from the decrease of Mn–Mn distance due to the incorporation of Al atoms. This behaviour is an additional property of the FSMA thin films apart from various other multifunctional properties and therefore, is of technological importance for their applications in magnetic storage devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.