Abstract
(Na0.5Bi0.5)0.4Sr0.6Ti1-xZrxO3 relaxor ferroelectric ceramic were prepared by a traditional ceramic preparation process introducing Zr4+ at the B-site. It was observed that introducing an appropriate amount of Zr4+ ions into the NBST matrix can improve the energy storage efficiency. (Na0.5Bi0.5)0.4Sr0.6Ti0.5Zr0.5O3 shows excellent energy storage density up to 2.83 J/cm3, and excellent efficiency (83.90 %) at 220 kV/cm. A single layer ceramic capacitor (SLCC) was also prepared by the tape casting technique for multilayer ceramic capacitors (MLCCs) to further enhance the energy storage performance. The recoverable energy storage capacity is increased to 4.52 J/cm3 and the efficiency is 70.02 % at 460 kV/cm. Moreover, it still has a relatively stable energy storage performance after 105 cycles of charge and discharge. This sample has exhibited outstanding energy storage performance, fatigue resistance, and charge/discharge performance and has great potential value in practical applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.