Abstract
The (0.9-x)[0.92Bi0.5Na0.5TiO3-0.08BaTiO3]-xSrZrO3-0.10NaNbO3 (x = 0, 0.02, 0.04, 0.06, 0.08, 0.10, abbreviated as BNTBT-100xSZ-NN) lead-free ferroelectric ceramics were prepared by conventional solid state reaction method. XRD Rietveld refinement indicates that R3c and P4bm phases coexist in the sample, while P4bm weakly polar phase accounts for a large proportion of 90%. BNT-100xSZ-NN shows broad permittivity peaks in the ɛ′-T curves. Slim P-E ferroelectric hysteresis loops are obtained due to the long range of ferroelectric order broken by the addition of SrZrO3 and NaNbO3 as well as the enhancement of the weakly polar region. The excellent energy storage properties are obtained at the composition of x = 0.08, which has high energy storage density of 0.95 J/cm3 at the electric field of 110 kV/cm and small variation (7%) in the temperature range of 25–175 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.