Abstract
In this work, a novel lead-free relaxor-ferroelectric ceramics of (1-x)(0.65BaTiO3-0.35Bi0.5Na0.5TiO3)-xSrY0.5Nb0.5O3 ((1-x)BTBNT-xSYN x = 0.02–0.12), was designed and prepared by the conventional solid state reaction method. The results show that all of the sintered samples have a perovskite structure. The Curie Temperature (Tc) moves to the low temperature side which causes the high dielectric constant at room temperature, and the ferroelectric hysteresis loop becomes slimmer and slimmer with increasing the content of SYN. Meanwhile, the optimal energy storage properties can be obtained in 0.92BTBNT-0.08SYN ceramic with an impressive discharged energy density (Wrec) of 1.36 J/cm3 under 152 kV/cm, and the charge-discharge efficiency reaches 74.3%. Therefore, all these results indicate that (1-x)BTBNT-xSYN lead-free ceramics can be applied for pulsed power capacitors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.