Abstract
In this work, we demonstrate a giant elastocaloric effect in a Ni50Mn33In14Si1Cu2 alloy. Owing to the large transformation entropy change and low thermal hysteresis, giant adiabatic temperature change (ΔTad) of − 18.2 K is obtained on unloading from a maximum compressive strain of 6 % with a low stress of 145 MPa. Moreover, large specific adiabatic temperature variation (ΔTad/σmax) up to 126 K/GPa has been achieved. This ΔTad/σmax value significantly exceeds those in the typical shape memory alloys. The present results demonstrate that the target alloy exhibits a distinct advantage in the strength of elastocaloric effect, being crucial for practical applications of solid-state refrigeration. In addition, it is found that the cyclic stability can be effectively enhanced by one-step overstress superelastic training for the first cycle.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.