Abstract
Ba0.85Ca0.15Zr0.10Ti0.90O3 (BCZT) lead-free ceramics demonstrated excellent dielectric, ferroelectric, and piezoelectric properties at the morphotropic phase boundary (MPB). So far, to study the effect of morphological changes on dielectric and ferroelectric properties in lead-free BCZT ceramics, researchers have mostly focused on the influence of spherical grain shape change. In this study, BCZT ceramics with rod-like grains and aspect ratio of about 10 were synthesized by surfactant-assisted solvothermal route. X-ray diffraction (XRD) and selected area electron diffraction (SAED) performed at room temperature confirm the crystallization of pure perovskite with tetragonal symmetry. Scanning electron microscopy (SEM) image showed that BCZT ceramics have kept the 1D rod-like grains with an average aspect ratio of about 4. Rod-like BCZT ceramics exhibit enhanced dielectric ferroelectric (ɛr = 11,906, tanδ = 0.014, Pr = 6.01 μgC/cm2, and Ec = 2.46 kV/cm), and electrocaloric properties (ΔT = 0.492 K and gZ = 0.289 (K·mm)/kV at 17 kV/cm) with respect to spherical BCZT ceramics. Therefore, rod-like BCZT lead-free ceramics have good potential to be used in solid-state refrigeration technology.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.