Abstract
The physical, chemical and mechanical properties of magnesium alloys make them attractive materials for automotive and aerospace applications. However, these materials are susceptible to corrosion and wear. This work discusses the potential of using sol-gel based coatings consisting of ZrO 2 and 15 wt.% of CeO 2 . The CeO 2 component provides enhanced corrosion protection, while ZrO 2 impart corrosion as well as wear resistance. Coating deposition was performed by the dip coating technique on two magnesium alloy substrates with different surface finishes: AZ91D (as-casted, sand-blasted, and machined) and AZ31 (rolled and machined). All as-deposited coatings (xerogel coatings) were then subjected to 10 h annealilng: a temperature of 180 °C was applied to the AZ91D alloy and 140 °C to the AZ31 alloy. Morphological and structural properties of the annealed coatings were investigated by scanning electron microscopy, atomic force microscopy and transmission electron microscopy. Coating composition was examined using energy dispersive X-ray analysis. Adhesion of the annealed ZrO 2 -CeO 2 coatings on the substrates, assessed by scratch tests, showed critical loads indicative of coating perforation of up to 32 N. Hardness and elasticity, measured using depth-sensing nanoindentation tests, gave a hardness and elastic modulus of 4.5 GPa and 98 GPa, respectively. Salt spray corrosion tests performed on these coatings showed superior corrosion resistance for AZ91D (as-casted and machined) and AZ31 (machined), while severe corrosion was observed for the AZ31 (rolled) and AZ91D (sand-blasted) magnesium alloy substrates.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.