Abstract
The accelerated age-hardening response and the enhanced peak-hardness in Al-Mg-Si with Zn addition was investigated by three-dimensional atom probe and transmission electron microscopy. The results showed that Zn addition significantly increased the number density of solute aggregates by stimulating the formation of more Mg-Si precipitates and resulted in a higher Mg/Si ratio because of the formation of Mg-Zn precipitates. A synergistic strengthening from Mg-Si and Mg-Zn-(Si) solute aggregates was estimated to accelerate the age-hardening response at the early aging stage, and that from β phases for Mg2Si system and Guinier-Preston (GP) I zones/η′ phases for MgZn2 system enhanced the peak-harness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.