Abstract
The metal–organic framework UiO-66-NH2 was synthesized in a scaled batch of approximately 100 g. The material was then pressed into small pellets at pressures ranging from 5000 to 100000 psi to determine the effects on porosity and crystal structure. Nitrogen isotherm data and powder X-ray diffraction data indicate that the structure remains intact up to 25000 psi, with only a slight decrease in surface area. The structure exhibits significant degradation at pressures above 25000 psi. Subsequently, the powder was pressed at 5000 psi and then crushed and sieved into 20 × 40 mesh granules for evaluation against ammonia and cyanogen chloride in a breakthrough system simulating individual protection filters and respirator cartridges. The MOF showed capacity similar to that of a broad-spectrum carbon for both ammonia and cyanogen chloride; however, the breakthrough times, especially for cyanogen chloride, were dramatically reduced, likely as a result of mass-transfer limitations from the completely microporous...
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.