Abstract
Groups of thirty 120-mm bore angular-contact ball bearings were endurance tested at a speed of 12 000 and 25 000 rpm (1.44 × 106 and 3.0 × 106 DN) and a thrust load of 66 721 N (5000 lb). The bearings were manufactured from a single heat of VIM-VAR AISI M-50 steel. At 1.44 × 106 and 3.0 × 106 DN, 84 483 and 74 800 bearing test hours were accumulated, respectively. Test results were compared with similar bearings made from CVM AISI M-50 steel run under the same conditions. Bearing lives at speeds of 3 × 106 DN with the VIM-VAR AISI M-50 steel were nearly equivalent to those obtained at lower speeds. A combined processing and material life factor of 44 was found for VIM-VAR AISI M-50 steel. Continuous running after a spall has occurred at 3.0 × 106 DN can result in a destructive fracture of the bearing inner race.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.