Abstract
The encapsulating annealing of N+ implanted 4H-SiC(0001) is performed using diamondlike- carbon (DLC) films for the suppression of surface roughening. 4H-SiC(0001) sample with an off-orientation of 8o is multiply implanted by N+ with energy ranging from 15 to 120 keV at a total dose of 2.4×1015 cm-2 at room temperature. DLC films with thickness ranging from 0.3 to 1.8 μm are deposited on the surface of implanted sample using plasma-based ion implantation equipment with C2H4 gas. The DLC capped sample is annealed at 1500 oC for 5 min using IR image annealer. After annealing, DLC film is removed by the oxidization. The sample capped by DLC film with a thickness of 0.3 μm shows the root mean square (RMS) surface roughness of 0.6 nm while the annealed sample without DLC film shows RMS surface roughness of 5.2 nm. As the thickness of DLC film is increased from 0.3 to 1.8 μm, the RMS surface roughness is decreased from 0.6 to 0.2 nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.