Emulsion of polyurethane having thermosetting properties. II. Relation between the mechanical properties of film and the polyurethane structure

Abstract

AbstractA self‐emulsifiable polyurethane emulsion having thermosetting property was prepared by the following procedure: the polyurethane–urea–amine was first prepared by the reaction of diethylene–triamine with a prepolymer containing terminal isocyanate groups in a ketone solvent, and then the primary amino group in the polyurethane–urea–amine was reacted with epichlorohydrin. The mixture was neutralized with an aqueous acid, and finally the ketone solvent was removed by distillation in vacuo. In the polyurethane, polytetramethylene glycol (PTMG) was the base polymer functioning as the soft segment. The present paper reports the effects of the following variables on the mechanical properties of the film prepared from the polyurethane emulsion, i.e., the Mn of PTMG, the molar ratio of diethylene–triamine (DTA) to prepolymer containing terminal isocyanate groups, the structure of the isocyanate end group and the molar ratio of tolylene diisocyanate (TDI) with PTMG. The best elastomer property was realized when Mn of PTMG was 2000, TDI/PTMG molar ratio was 2.0, and prepolymer/DTA molar ratio was 0.85.