Тemplate synthesis of multidimensional porous silica

T F Kouznetsova,Ju D Sauka,O V Luksha,O L Zhigalova,A I Ivanets,O N Opanasenko

doi:10.29235/1561-8331-2020-56-1-42-50

Abstract

Isothermal data of superficial tension of solutions of surfactant mixture and low-temperature nitrogen sorption of multidimensional porous silica received by template synthesis prove complementarity of its properties and properties of SAA micelles. The measured isotherms of gas sorption belong to IV Type inherent in mesoporous adsorbents. The BET specific surface area is 600–800 m2/g, and the Gurvich pore volume is 0.7–1.0 cm3/g. With increase in mole fraction of nonionic component these values decrease, the ordered texture of SiO2, characteristic of MCM-48 mesoporous molecular sieve, collapses, d211-spacing becomes < 3.31 nm, and NLDFT distribution is transformed from monomodal to polymodal one.

Highlights

Isothermal data of superficial tension of solutions of surfactant mixture and low-temperature nitrogen sorption of multidimensional porous silica received by template synthesis prove complementarity of its properties and properties of SAA micelles
A new family of mesoporous molecular sieves prepared with liquid crystal templates / J
Information about the authorsTatyana F. Kouznetsova – Ph. D. (Chemistry), Head of the Laboratory. Institute of General and Inorganic Chemi stry, National Academy of Sciences of Belarus (9/1, Surga nov Str., 220072, Minsk, Republic of Belarus). E-mail: tatyana. f k@gmail.com Andrei I. Ivanets – D. Sc. (Chemistry), Leading Rese archer. Institute of General and Inorganic Chemistry, Natio nal Academy of Sciences of Belarus (9/1, Surganov Str., 220072, Minsk, Republic of Belarus). E-mail: andreiivanets@ ya.ru Olga N. Opanasenko – Ph. D. (Chemistry), Head of the Laboratory. Institute of General and Inorganic Chemistry, National Academy of Sciences of Belarus (9/1, Surganov Str., 220072, Minsk, Republic of Belarus). E-mail: ionch@ igic.bas-net.by Oksana L. Zhigalova – Ph. D. (Chemistry), Senior Rese archer. Institute of General and Inorganic Chemistry, Natio nal Academy of Sciences of Belarus (9/1, Surganov Str., 220072, Minsk, Republic of Belarus). E-mail: zhigalova.o@ mail.ru

Summary

МАТРИЧНЫЙ СИНТЕЗ МНОГОМЕРНОГО ПОРИСТОГО КРЕМНЕЗЕМА

Изотермические данные поверхностного натяжения растворов смеси поверхностно-активных веществ и низкотемпературной сорбции азота многомерным пористым кремнеземом, полученным путем матричного синтеза, доказывают комплементарность его свойств и свойств мицелл ПАВ. Измеренные изотермы газовой сорбции относятся к типу IV, присущему мезопористым адсорбентам. Удельная поверхность по БЭТ составляет 600–800 м2/г, а объем пор по Гурвичу – 0,7–1,0 см3/г. С увеличением молярной доли неионного компонента значения данных величин уменьшаются, упорядоченная текстура SiO2, характерная для мезопористого молекулярного сита МСМ-48, разрушается, межплоскостное расстояние d211 становится < 3,31 нм, и NLDFT-распределение из мономодального трансформируется в полимодальное. Ключевые слова: матричный синтез, МСМ-48, мезопористые адсорбенты, капиллярно-конденсационный гистерезис. Mатричный синтез многомерного пористого кремнезема / Т.

Список использованных источников

Information about the authors