Abstract
The multilayered structure thin films (Gd2(MoO4)3:Ho(Tm)/Yb@Gd2(MoO4)3:Yb)) were prepared through sol–gel and spin-coating method, while the average thinness was nearly 140 nm. We investigated the up-conversion luminescence of Gd2(MoO4)3:Ho(Tm)/Yb@Gd2(MoO4)3:Yb thin films. The results show that the double-layer structured thin films are able to increase the emission intensity. The fluorescence enhancement factors of the luminescence from Gd2(MoO4)3:Ho/Yb@Gd2(MoO4)3:Yb thin films, located at 540 and 662 nm, reach 7.5 and 4.3, respectively. And the enhancement factors of emissions located at 450, 475 and 650 nm (Gd2(MoO4)3:Tm/Yb@Gd2(MoO4)3:Yb)) reach 9, 2 and 2, respectively. The considerable enhancement is due to the suppression of surface quenching and energy harvesting via the Yb ions in the outer shell. In addition, the emission color of thin films can be modulated from yellow to blue via tuning the number of Gd2(MoO4)3:Ho/Yb and Gd2(MoO4)3:Tm/Yb layers, which provides a feasible strategy to tune the up-conversion emission color.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.