Most transparent conducting materials are based on Sn:In2O3 (ITO). When applied onto flexible substrates, ITO can be prepared in an oxide–metal–oxide (OMO) configuration, typically ITO/Ag/ITO, where the ductility of the embedded metal layer is intended to reduce the mechanical brittleness and improve the electrical conductivity of the OMO multilayer. Hitherto, the lower limit of the thickness of the Ag layer has been limited by the percolation threshold, which limits the Ag layer to be thicker than ∼10 nm to avoid agglomeration and to ensure conductivity and structural stability. Metal layers of thicknesses below 10 nm are, however, desirable for obtaining OMO coatings with better optical properties. It is known that agglomeration of the metal layer can, to some extent, be suppressed when substituting Ag by an Ag–Pd–Cu (APC) alloy. APC-based OMO films exhibit excellent optical and electrical properties, but still continuous APC films well below 10 nm thickness cannot be achieved. In this work we demonstrate that controlled oxidation of APC results in smooth, ultrathin APC:O continuous coatings (of thickness ∼5 nm) on ITO-coated PET substrates. Moderate oxidation yields superficial PdOx formation, which suppresses Ag agglomeration, while still maintaining excellent conductivity. On the other hand, extensive oxidation of APC leads to extensive Pd oxide nucleation deteriorating the conductivity of the film. The ITO/APC:O/ITO films exhibit low resistivity, attributed to a high Hall mobility associated with suppressed agglomeration, good stability in high humidity/temperature environments, superior transmittance in the visible and infrared region, and excellent mechanical bending properties, thus providing new opportunities for fabricating superior transparent conducting coatings on polymer substrates.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.