Elution from direct composites for provisional restorations.

Abstract

Purpose To assess elution from direct composite materials for provisional restorations and compare them with elution from direct restorative composites for permanent restorations.Methods Two dual-cure (Integrity Multi-Cure and Tempsmart DC) and two self-curing composites (Protemp 4 and Structur 3) were used, with Essentia serving as a reference. Cylindrical specimens (n=20) were cured according to the manufacturer's instructions; the dual-cure materials were prepared in both self- and dual-curing modes. Elution experiments were performed using water and absolute ethanol. The samples were incubated at 37 °C for either 24 h or four weeks; the extraction solvents were refreshed weekly. The eluted BisEMA (-3 / -6 / -10), BisGMA, CQ, UDMA, and TEGDMA were quantified using UHPLC-MS/MS.Results Monomer elution was detected in all provisional composites at 24 h and four weeks, but the amounts released did not exceed those released by the reference composite. When prepared in self-curing mode, Integrity Multi-Cure exhibited significantly higher elution of BisEMA-3, -6, and -10 in ethanol both after 24 h and cumulatively after four weeks. Self-cured Tempsmart DC released significantly more CQ, TEGDMA, and UDMA in both water and ethanol after immersion for 24 h and four weeks, along with significantly more BisGMA in ethanol both after 24 h and four weeks comparison to dual-cured Tempsmart DC (two-way ANOVA, post-hoc Tukey, P < 0.05).Conclusions Provisional composite materials did not elute higher amounts of monomers than a restorative composite. Dual-cured materials, prepared in the self-curing mode, show a trend towards higher monomer elution.