Abstract
Particle disease from the release of metal, cement, ceramic, or polyethylene particles is a rare condition in total knee replacement. Wear, fracture, or corrosion of the components leads to foreign body reaction in the joint, followed by pain, swelling, limited motion, difficulty in walking, functional disability, and occasional systemic disease. This paper presents two cases of metal-on-cement disease as an etiology for the implant failure wherein the metal particles were shed off from the implant, along with cement and polyethylene particles, leading to a complex foreign body reaction in the failed total knee. We have coined this phenomenon as "cementallosis."Initial symptoms and signs from implant failure in both patients were mild, intermittent mediolateral knee pain that was aggravated after walking but no pain at rest or at night. The pain was associated with a 'buckling' sensation, recurrent knee swelling, and gradually worsening knee range of motion. Clinical examination in both cases was suggestive of a well-healed anterior midline surgical scar, mild to moderate effusion, mild diffuse tenderness over the entire joint, limited functional range of motion, grade 1+ laxity throughout the range of motion, and intact distal neurovascular status. Routine blood and synovial fluid workup were inconclusive for identifying the exact etiology of the patient’s symptoms. Radiographs, computed tomography (CT) scans, as well as bone scans, were negative for prosthetic joint infection, component malalignment, polyethylene wear, maltracking, or loosening of the components but showed mild to moderate effusions, synovial hypertrophy, and mild scattered periprosthetic osteolysis. Intraoperatively, there was significant synovial hypertrophy with dark pigment deposition and apparent dissociation of the femoral and tibial components from the underlying cement mantle, although the cement was well-adhered to the underlying bone. Synovial fluid and multiple tissue specimens were suggestive of complex foreign body granulomas with metal, cement, and polyethylene particles. These patients had undergone surgery by the same surgery team in the community using the same implant.These cases demonstrate the failure of a total knee arthroplasty implant at the metal-cement interface with features of adverse local tissue reactions that resemble a pseudotumor from the metal-on-metal disease in the knee joint. We have compared and contrasted the clinical presentations, laboratory, imaging, histopathological, and intraoperative study findings in these cases. Knowing what to look for will aid in early diagnosis, ordering necessary investigations, better surgery planning, reducing operative time, as well as improving outcomes and cost of care. The aim of this paper is to educate the audience about this new phenomenon as a cause of knee prosthesis failure produced by a complex pseudotumor-like foreign body reaction that involves metal, cement, and polyethylene particles.
Highlights
Metal-on-cement disease is a rare condition in which corrosion and wear of the femoral, tibial, or metalbacked patella components occur due to broken cement-metal bonding in cemented primary or revision total knee replacement
The aim of this paper is to educate the audience about this new phenomenon as a cause of knee prosthesis failure produced by a complex pseudotumor-like foreign body reaction that involves metal, cement, and polyethylene particles
This paper presents two cases who had unclear etiology for their implant failure and were later diagnosed with complex metalon-cement disease
Summary
Metal-on-cement disease is a rare condition in which corrosion and wear of the femoral, tibial, or metalbacked patella components occur due to broken cement-metal bonding in cemented primary or revision total knee replacement. Metal and cement debris further lead to third-body wear, and abrasive polyethylene wears, progressing to a slow and silent catastrophe. Existing literature lacks adequate information on the mechanisms and reasons for the failure of the total knee implant at the metal-cement interface. The implant failure commonly occurs from abrasion, fracture, fretting, fatigue, or adhesive wear [1]. This paper presents two cases who had unclear etiology for their implant failure and were later diagnosed with complex metalon-cement disease
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.