Abstract
Elongated wire-like Zinc oxide, nanocombs and nanocrystals have been successfully synthesized on the silicon substrate from the metallic zinc as a starting material. The annealing temperature was as low as 450 ºC in argon atmosphere mixed with about 3% oxygen. Structural analysis using the X-ray Diffraction (XRD) and Transmission Electron Microscopy (TEM) showed that the existence of two phases; nanowires and crystalline form. Moreover some nanoparticles aggregates were noticed to be attached in the bulk to the sides of the ZnO nanocrystals and sometimes these aggregate attached to the Zinc oxide hexagonal crystal and grow to form nanowire at different angles. Scanning electron microscopy (SEM) investigations for the zinc oxide nanostructure on the silicon substrate showed the formation of the nanocrystals in the gas flow direction and at the low energy sites over the silicon substrate. Photoluminescence (PL) measurements, performed at the room temperature, showed the existence of two basic emissions: narrow ultraviolet (UV) emission at 398 nm which attributed to the near band edge emission of the wide band gap and a very wide, more intensive, green emission at 471 nm corresponds to the crystal defects such as vacancies, interstitial sites in ZnO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.