Abstract
CoCrAlY+WC-Co and CoCrAlY+Cr3C2-NiCr coatings are deposited on nickel based alloy using atmospheric plasma spray technique. Mechanical properties such as microhardness, adhesion strength and fracture toughness of coatings are evaluated. Elevated temperature solid particle erosion behaviour of these coatings are investigated at 600 °C using alumina erodent at 30 and 90° impact angle. Coatings are characterized utilizing Scanning electron microscope (SEM), x-ray diffraction (XRD) and Energy dispersive spectroscopy (EDS). CoCrAlY+WC-Co coating shows higher hardness, adhesion strength and fracture toughness than CoCrAlY+Cr3C2-NiCr coating. CoCrAlY+WC-Co coating exhibited approximately 3 times higher erosion resistance than CoCrAlY+Cr3C2-NiCr coating at 90° and 30° impact angles. SEM images of eroded surfaces of coatings reveals the combination of ductile and brittle fracture. CoCrAlY+Cr3C2-NiCr coating shows severe cracks, craters, carbide pull out and chipping than CoCrAlY+WC-Co coating. High temperature erosion is a combination of simultaneous building up of material by oxidation and removal of material by erosion process. Thus reforming the erosion process to oxidation modified erosion process.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.