Abstract
A new medium-entropy superalloy was produced based on the compositions of equiatomic CrCoNi and Ni-base superalloy Inconel 740H. Initial alloy design was performed using Thermo-Calc. The aging response and microstructural stability were assessed following heat treatment at temperatures between 600 and 900 °C and durations up to 100 h. Aging from a fully recrystallized state resulted in negligible grain growth and produced γ’ and σ phases. The same phases were present after aging from a cold-rolled state, but partially recrystallized microstructures resulted in multi-modal size distributions and heterogeneous spatial arrangements. Room temperature hardness measurements were used to correlate aging conditions with quantitative precipitate measurements and mechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.