Abstract
Abstract The elemental micro-segregation characteristic within the weld zone for ytterbium fiber laser welded Hastelloy C-276 sheet was investigated. The analysis of segregation ratio and equilibrium distribution coefficient of elements, determined through EDS data, indicate the reduction in micro-segregation of elements compared with the previous reported literatures for laser welded Hastelloy C-276. High melting efficiency of ytterbium fiber laser, reduction in the amount of linear heat input, and high cooling rate of the mushy zone lead to the reduction in micro-segregation. The melting efficiency of ytterbium fiber laser for welding of Hastelloy C-276 of 64% is higher than that (48%) of conventional welding methods. High melting efficiency leads to the reduction in the linear heat input required for welding. Hence, in the present investigation, the same was found to substantially reduce as compared to the previous reported literature. The cooling rate from liquidus temperature to solidus temperature at the weld centerline was found to be in the order of 103 °C/s. Cellular dendritic substructure that constituted for lower micro-segregation was formed at the weld centerline.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.