Abstract
In this paper, a simple and effective method was applied to enhance regenerated silk fibroin (RSF) mats electrospun from aqueous solution. The mats were first mechanically drawn in 90vol.% ethanol aqueous solution and then immersed in the same solution for 30min. The morphology, structure, thermal and mechanical properties of the RSF mats with different draw rates and draw ratios were investigated by scanning electron microscope (SEM), Raman spectroscopy, wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC) and tensile test. Results revealed that the content of β-sheet conformation, the crystallinity and the number of fibers aligned to the drawing direction increased evidently with the draw ratio. The breaking strength and breaking energy of the post-treated mats at 1.4× draw ratio and 0.1mm/s draw rate were 8.6MPa and 172.2J/kg, respectively. However, those of the as-spun mats were only 1.8MPa and 93.2J/kg, respectively. The enhanced RSF mats prepared from entirely aqueous solutions may have extensive applications for tissue engineering.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.