Abstract
In this paper, we report a comparison of interfacial reactions of Sn-3.8Ag-0.7Cu (SAC 387) and SAC (0-1.5 Zn) solder pastes on Cu (organic solderability preservative finish) and Au/Ni-P/Cu [electroless Ni immersion gold (ENIG)] substrate metallizations with Ni/Sn and Cu/Sn plated component leads. Zn added to the paste in the form of surface-coated micrometer-sized particles dissolves into the solder during reflow. High-temperature aging (150 °C and 185 °C), thermal cycling experiments ( -20°C to 175 °C for FR4 substrate, -40°C to 185 °C for ENIG polyimide substrate), and shear testing of the solder joints were carried out. At a Cu interface, adding Zn to the solder joint improves the shear strength and suppresses Cu3Sn and overall interfacial intermetallic compound (IMC) and Kirkendall void formation . However, above this temperature, the presence of Zn accelerates IMC growth. At a Ni interface, IMC suppression with Zn was noted at all temperatures. The amount of IMC suppression depends on the Zn concentration in the IMCs, which in turn depends on the geometry of joint as well as the original concentration of Zn in the solder.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IEEE Transactions on Components, Packaging and Manufacturing Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.