Abstract
The structure and physical properties of highly conductive Langmuir-Blodgett films of tridecylmethylammonium-Au(dmit)2 (3C10-Au) are described. The layered structure of the film was revealed by X-ray diffraction method. The d-spacing was 1.9 and 2.7 nm for the film before and after oxidation, respectively. The conductivity of the LB films of 3C10-Au after oxidation was 30 – 50 S/cm at room temperature, showing a metallic temperature dependence down to around 150 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.