Abstract
We present experimental XMLD spectra measured on epitaxial (001)-oriented thin Co2FeSi films, which are rich in features and depend sensitively on the degree of atomic order and interdiffusion from capping layers. Al- and Cr-capped films with different degrees of atomic order were prepared by DC magnetron sputtering by varying the deposition temperatures. The local structural properties of the film samples were additionally investigated by nuclear magnetic resonance (NMR) measurements. The XMLD spectra of the different samples show clear and uniform trends at the L3,2 edges. The Al-capped samples show similar behavior as previous measured XMLD spectra of Co2FeSi0.6Al0.4. Thus, we assume that during deposition Al atoms are being implanted into the subsurface of Co2FeSi. Such an interdiffusion is not observed for the corresponding Cr-capped films, which makes Cr the material of choice for capping Co2FeSi films. We report stronger XMLD intensities at the L3,2 Co and Fe egdes for films with a higher saturation magnetization. Additionally, we compare the spectra with ab initio predictions and obtain a reasonably good agreement. Furthermore, we were able to detect an XMCD signal at the Si L-edge, indicating the presence of a magnetic moment at the Si atoms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.