Abstract
Using electron spin resonance, lattice position and dynamic properties of Mn2+ ions were studied in 0.5 and 2 % manganese doped SrTiO3 ceramics prepared by conventional mixed oxide method. The measurements showed that Mn2+ ions substitute preferably up to 97 % for Sr if the ceramics is prepared with a deficit of Sr ions. Motional narrowing of the Mn2+ ESR spectrum was observed when temperature increases from 120 K to 240-250 K that was explained as a manifestation of off-center position of this ion at the Sr site. From the analysis of the ESR spectra the activation energy Ea = 86 mV and frequency factor 1/?0 ? (2-10)x10^(-14) 1/s for jumping of the impurity between symmetrical off-center positions were determined. Both values are in agreement with those derived previously from dielectric relaxation. This proves the origin of dielectric anomalies in SrTiO3:Mn as those produced by the reorientation dynamics of Mn2+ dipoles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.