Abstract
The wetting reaction between molten eutectic SnPb solder and a sputtered trilayer Cu/Ni(V)/Al thin film metallization was studied using cross-sectional transmission electron microscopy and scanning electron microscopy. Reaction temperatures were from 200 to 240 °C and reaction times ranged from 1 to 40 min. The initial reaction products were Cu6Sn5 and Cu3Sn. The latter transforms to the former after an annealing greater than 1 min at 220 °C. The Cu6Sn5 grains adhere well to the Ni(V) surface and no spalling of them was observed, even after 40 min at 220 °C. This surprising result indicates that the Cu/Ni(V)/Al or Cu6Sn5/Ni(V)/Al is a stable thin film metallization for low temperature eutectic SnPb solder direct chip attachment to organic substrates. Additionally, Kirkendall voids accompanied Cu3Sn formation, yet the voids disappear when the Cu3Sn transforms to Cu6Sn5.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.