Electron microscopy studies of octa-calcium phosphate thin films obtained by pulsed laser deposition

Abstract

Octa-calcium phosphate (OCP), Ca8(HPO4)2(PO4)4·5H2O, is present as transient compound in the precipitation of hydroxyapatite (HA) and biological apatites. Because of these characteristics, OCP plays a crucial role in the in-vivo mineralization of human bones and teeth. The use of OCP in developing new generations of bone prosthesis stands therefore for an innovative challenge. This paper reports studies of OCP structures grown in the form of thin films by pulsed laser deposition (PLD) with emphasis on electron microscopy investigations. OCP films were grown on etched Ti substrates, using an UV KrF* excimer laser source (λ=248 nm, τ≥20 ns). Films were deposited in low-pressure (50 Pa) water vapors environment on substrates heated at 20–180 °C. We performed annealing treatments in water vapors and ambient pressure at substrate temperatures identical to those used during deposition. Comprehensive structural and morphological investigations were carried out with different based-electron microscopy procedures. Grazing incidence X-ray diffraction (GIXRD) and white light confocal microscopy were also applied to characterize the films. Ca/P atomic ratio of films was determined by energy dispersive X-ray spectrometry, electron energy loss spectroscopy and X-ray photoelectron spectroscopy. The obtained films generally exhibit an amorphous structure, as evidenced by GIXRD. Nevertheless, cross-section transmission electron microscopy investigations provide supplementary information about the film characteristics and material crystallization in small domains. OCP nanoparticles coalesce and grow perpendicular to the substrate in a tree-like structure, comparable to a coral reef.