Abstract
Three types of biomaterials based on hydroxyapatite are synthesized and investigated. Hydroxyapatite nanocrystals or microcrystals precipitated from low-temperature aqueous solutions serve as the initial material used for preparing spherical porous granules approximately 300–500 μm in diameter. Sintering of hydroxyapatite crystals at a temperature of 870°C for 2 h or at 1000°C (for 3 h) + 1200°C (for 2 h) brings about the formation of solid ceramics with different internal structures. According to the electron microscopic data, the ceramic material prepared at 870°C is formed by agglomerated hydroxyapatite nanocrystals, whereas the ceramics sintered at 1200°C (with a bending strength of the order of 100 MPa) are composed of crystal blocks as large as 2 μm. It is established that all the biomaterials have a single-phase composition and consist of the hydroxyapatite with a structure retained up to a temperature of 1200°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.